新能源电池连接器铜铝电路的连接技术电缆组件

铜的密度为8.9×10 3公斤/立方米，铝的密度是2.7×10 3公斤/立方米，且铝质量密度小于三分之一的铜的。铜和铝的现货价格示于下面的两个图。铝是小于4/1铜。在整个行业，我们正在努力，以减少重量和成本。这是我们与铝代替铜钢板在每一个可能的环节最简单实用的方法。本文的问题和铜铝连接的解决方案的交易。

As for the selection of replacing copper bar and copper cable with aluminum bar aluminum cable, if you look at the basic parameters, the resistivity of red copper is 0.018 Ω * m m 2 / m, the resistivity of aluminum is 0.027 Ω * mm2 / m, and the cross section of the same size, the conductivity of aluminum is 2 / 3 of copper, and the weight is 1 / 3 of copper, it is cost-effective to use aluminum. The problem is that the aluminum bar of copper bar cannot be directly overlapped, especially in humid environment. According to the conventional connection mode of copper bar, screw the joint to a piece with large screws. In a short time, it will be found that there is a large amount of oxide layer at the joint position and the resistance increases significantly. Why is that?

金属的电化学腐蚀

什么是电话的铜和铝之间的腐蚀？当铜和铝导线直接连接，这两种金属的接触表面容易水分，二氧化碳和空气中的其它杂质的作用下形式电解质，从而形成一次电池与铝作为负极和铜作为正极（为什么铝必须是负电极，电子的损失主要是由元件本身的电势来确定，见下文的表中为元件电位），这将导致的铝和铜的接触电化学腐蚀在铝连接电阻增加。

另外，由于弹性模量和铜和铝的热膨胀系数有很大的不同，在操作许多冷热循环（通电和断电）后，接触点会产生大的间隙，这将影响接触和增加接触电阻。接触电阻的增加，温度会在操作期间上升。在耐高温，耐腐蚀和氧化作用将加剧，造成恶性循环，连接质量的进一步恶化，并最终导致高接触点温度，甚至抽烟，燃烧等事故。

当在高温环境下长时间的联合工程，将通过机械振动的影响，这将导致铜和铝原子的扩散而形成的金属间化合物层和连续地变厚，这将减少关节的冲击韧性和增加电阻。有金属，这是不能隔离的二氧化碳和水蒸汽，以及上述原电池反应可能发生的环境之间提供气泡的空气间隙。

为了避免电化学腐蚀，有必要除去的基本条件，以形成原电池的电解液中，除去水蒸汽或隔离空气。